Application of stainless steel in dental instruments


Dental stainless steel alloy - dental steel

Steel is the most common alloy in the world.
Its properties are well known. And due to alloying agents, it can be given any desired properties. Dental steel is very cheap.

Among the disadvantages: steel is heavy (density about 8 g/cm3) and chemically active. May cause allergies, galvanosis.

Stainless steel in orthopedic dentistry - grades:

STEEL GRADE 1X18H9T (EYA-1)

Dental alloy for crowns COMPOSITION :

1.1% carbon; 9% nickel;18% chromium; 2% manganese, 0.35% titanium, 1.0% silicon, the rest is iron.

Used for fixed prostheses: individual crowns, cast teeth, facets.

STEEL GRADE 20Х18Н9Т

COMPOSITION: 0.20% carbon, 9% nickel, 18% chromium, 2.0% manganese, 1.0% titanium, 1.0% silicon, the rest is iron.

The following are produced from this type of steel in the factory:

· standard sleeves used for the production of stamped crowns;

· clasp blanks (for ChSPP)

· elastic metal matrices for filling, as well as separation strips

· STEEL for dentistry GRADE 25Х18Н102С

COMPOSITION: 0.25% carbon, 10.0% nickel, 18.0% chromium, 2.0% manganese, 1.8% silicon, the rest is iron.

APPLICATION: manufactured in the factory:

· teeth (lateral upper and lower) for stamped-soldered bridges;

· frames for metal-plastic bridges, for cladding;

· orthodontic wire with a diameter from 0.6 to 2.0 mm (step 0.2 mm)

Silver solder is used as solder for non-precious alloys

Contains silver - 37%, copper - 50%, Manganese - 8-9%, Zinc - 5-6%

Source

Alloys in orthopedic dentistry

Metal occupies a central place among materials in dentistry. Most fixed dentures and removable denture frames are cast (or stamped) from dental alloys. Alloys in dentistry are used as auxiliary materials for soldering and stamping. Dental instruments are made from them.

  • Classification of metals and alloys in dentistry
  • Structural metal alloys in orthopedic dentistry
  • Noble metal alloys in dentistry
  • Base alloys in orthopedic dentistry
  • Auxiliary metal alloys in dentistry

Primary requirements

The important properties that metals and alloys in dentistry must have are:

  • high biological compatibility;
  • resistance to corrosion and tarnishing;
  • maintaining constant volume and shape;
  • safety, no toxicity;
  • inertness in the oral cavity;
  • mechanical properties (strength, hardness, rigidity, wear resistance, ductility);
  • physical properties (density, malleability, thermal conductivity, melting point);
  • aesthetic indicators;
  • hygienic properties (ease of cleaning with standard dental care products; in the case of using metal dentures, patients should not feel a metallic taste);
  • technological characteristics (ease of preparation and processing, segregation).

This is interesting: Clasp dentures, patient reviews, recommendations from dentists
Alloys that are intended for ceramic coating must meet the following criteria:

  • connects well with porcelain;
  • the temperature when processing the alloy should be higher than the temperature when processing porcelain;
  • the thermal expansion value of the alloy should be equal to the CTE of porcelain.

An important aspect is shrinkage, which occurs during the transformation of the liquid state of the metal into a solid state.

If the shrinkage is too high, it makes the fabrication of dental structures difficult. Ease of metal casting is important to every dental technician. The lower the temperature when melting and pouring, the easier it is to work with them.

The characteristics of metals must necessarily meet the requirements associated with their purpose and processing methods.

Metals and alloys in dentistry Classification

All metals and alloys are divided into ferrous and non-ferrous.

Ferrous metals are iron and alloys based on it. Steel and cast iron. Cast iron contains more than 2.14% carbon. Not used in dentistry.

The surface of cast iron is matte and non-shiny. It is difficult to polish.

Steel in dentistry

an iron-based alloy containing less than 2.14% carbon. In addition to iron and carbon, steel also contains other metals. They give the alloy new properties (alloy steel), including making it stainless.

Steel copings for stamping crowns

Alloy steel is an alloy of iron and carbon, with the addition of any other metals. They change the properties of the alloy (melting point, hardness, ductility, malleability, etc.).

Alloy steel

Stainless steel is corrosion resistant steel. Chromium (21%), as well as other metals, are most often used as an anti-corrosion agent.

Non-ferrous metals are, respectively, all other metals.

Metals in orthopedic dentistry are divided into noble and non-noble.

Noble metals (or precious metals) are metals that are resistant to corrosion and chemically inert. The main noble metals are gold, silver, and platinum group metals (platinum, palladium, iridium, osmium, etc.).

Base metals are metals that corrode easily and are not found in nature in their pure form. They are always mined from ores.

Purpose

Several decades ago, dentists made medical structures exclusively from noble metals in their pure form.
Gradually, a trend emerged to use them as various alloys. Closer to the 20th century, orthopedic dental appliances made of base metals , in particular alloys of steel and chromium, were common.

Base metals are very hard, which complicates their processing, but thanks to this feature, prostheses can be made of any length.

Pure gold was no longer used due to its insufficient hardness. Today, gold-palladium, gold-platinum, silver-palladium alloys are in demand because they are more durable, resistant to corrosion and have many other positive characteristics.

Base metal alloys are also popular.

They are excellent for ceramic coatings because the oxide film that appears on the surface promotes a strong bond.

Noble metals in dentistry and alloys

Noble metals in dentistry are expensive. But despite this, they continue to be used due to their excellent biocompatibility. They are not subject to corrosion, do not react with saliva, and do not cause allergies or intoxication.

A gold alloy may often be the only option for patients with polyetiological contact allergies.

Noble alloys are durable. Their only drawback (besides the price) is their softness and susceptibility to abrasion.

Gold alloys in dentistry.

COMPOSITION: 90% gold, 4% silver, 6% copper.

PROPERTIES: melting point 1063°C.

The alloy is characterized by ductility and can be easily machined under pressure (stamping, rolling, forging).

Due to its low hardness, the alloy wears off easily. Therefore, when making stamped crowns, solder is poured from the inside, onto the chewing surface or cutting edge.

Produced: in the form of disks with a diameter of 18, 20, 23, 25 mm and blocks of 5 g.

Application: for stamped crowns and bridges made of

alloy of precious metals in orthopedic dentistry

Consists of Gold – 75%, Silver and copper 8% each, and Platinum – 9%

Platinum gives this alloy elasticity and reduces shrinkage during casting.

Used for the manufacture of cast gold parts of clasp dentures, clasps and inlays

  • Dental gold alloy 750 standard (ZlSrKdM)

Cadmium is added to the composition - 5-12%.
Due to cadmium, the melting point of the alloy is reduced to 800 C. (The average melting point of gold alloys is 950-1050 C.) Which allows this alloy to be used as solder.

Silver-palladium alloy in dentistry

Silver-palladium alloys are distinguished by a higher melting point = 1100-1200 C. Their physical and mechanical properties are similar to gold alloys. But corrosion resistance is lower. (Silver darkens when in contact with sulfur compounds) Alloys are ductile and malleable. Soldered with gold solder (ZlSrKdM).

COMPOSITION: 75.1% silver, 24.5% palladium, some alloying metals (zinc, copper, gold).

Used for stamped crowns. They are produced respectively in the form of disks of various diameters (18, 20, 23, 25 mm) and 0.3 mm thick.

Composition: 78% silver, 18.5% palladium, other metals.

Used as an alloy for casting in dentistry.

The amount of palladium was reduced to 14.5%, silver was increased.

Application

Crowns, fillings, bridges, dentures, dental instruments, and more are made from all sorts of combinations of alloys and metals.

Materials for creating dental crowns that are especially popular are a combination of metal and ceramics.

A metal base made from alloys of noble metals such as gold, silver, platinum or palladium has a number of advantages compared to a base made from inexpensive materials:

  1. Gold-based alloys are durable, can withstand heavy chewing loads, have an antibacterial effect, and are unable to cause an allergic reaction, darkening or inflammation of the gums.
  2. Silver-palladium alloys are more ductile and affordable, but their quality is significantly lower than gold-containing alloys. Temporary crowns are most often made of stainless steel and aluminum.
  3. Titanium is widely used as a material for creating crowns, solid bridges, and prostheses. Its mechanical characteristics are not inferior to some noble alloys used for dental purposes.
    A persistent oxide film is formed on the titanium coating, thanks to which it is corrosion-resistant and biologically compatible with the tissues of a living organism.

    In addition, it is lightweight, so patients feel comfortable while wearing removable orthodontic appliances with a titanium base.

  4. An alloy of silver and mercury is used as a filling material. It is quite hard and durable, but raises some concerns due to the mercury content and a possible negative effect on the filling.
    Only a highly qualified dentist should place a filling made from such an alloy, since the placement technology presents certain difficulties.
  5. Metals such as nickel, titanium, silver, chromium-nickel corrosion-resistant steels are ideal for the manufacture of implants.
    Implants are subject to rejection by biological tissue, as well as deformation, heavy chewing and mechanical loads.

    Therefore, the materials for their manufacture must have good biological compatibility, strength and corrosion resistance.

  6. High-hardness tungsten steel is used to make dental cutting instruments. Cheaper steel is used for probing instruments, and dispersion-hardening stainless steel is used for microtools.

Dental stainless steel alloy - dental steel

Steel is the most common alloy in the world. Its properties are well known. And due to alloying agents, it can be given any desired properties.

Dental steel is very cheap.

Among the disadvantages: steel is heavy (density about 8 g/cm3) and chemically active. May cause allergies, galvanosis.

Stainless steel in orthopedic dentistry - grades:

  • STEEL GRADE 1 X 18 H 9T (EYA-1)

Dental alloy for crowns COMPOSITION:

1.1% carbon; 9% nickel;18% chromium; 2% manganese, 0.35% titanium, 1.0% silicon, the rest is iron.

Used for fixed prostheses: individual crowns, cast teeth, facets.

  • STEEL GRADE 20Х18Н9Т

COMPOSITION: 0.20% carbon, 9% nickel, 18% chromium, 2.0% manganese, 1.0% titanium, 1.0% silicon, the rest is iron.

The following are produced from this type of steel in the factory:

  • standard sleeves used for the production of stamped crowns;
  • elastic metal matrices for filling, as well as separation strips

STEEL for dentistry GRADE 25Х18Н102С

COMPOSITION: 0.25% carbon, 10.0% nickel, 18.0% chromium, 2.0% manganese, 1.8% silicon, the rest is iron.

APPLICATION: manufactured in the factory:

  • teeth (lateral upper and lower) for stamped-soldered bridges;
  • frames for metal-plastic bridges, for cladding;
  • orthodontic wire with a diameter of 0.6 to 2.0 mm (step 0.2 mm).

Silver solder PSR-37 or Cet solder is used as solder for non-precious alloys

Rina.

Contains silver - 37%, copper - 50%, Manganese - 8-9%, Zinc - 5-6%

Melting point – 725-810 C

Classification

Metals are classified into two main groups - ferrous and non-ferrous. Ferrous materials include iron, iron-carbon alloys, cast iron, and steel.

Non-ferrous - aluminum, copper, zinc, nickel. Modern dentists use more than 400 alloys based on various metals.

They are divided into the following groups:

  1. Noble.
  2. Ignoble.
  3. Solders (precious or non-precious materials used for soldering).

Noble

The cost of noble metals and the alloys they contain is quite high. At the same time, they enjoy deserved popularity because they have an invaluable quality for medical use - biocompatibility.

This is interesting: What types of dentures are there in the absence of teeth: the best options for jaw prosthetics

They are not familiar with the negative effects of corrosion; they do not come into contact with salivary secretions, which are constantly present in the oral cavity and have a detrimental effect on metal structures of a more “primitive” content.

Components made from precious elements do not cause individual intolerance to the material, fraught with outbreaks of allergies, and do not belong to the group of compounds that can cause intoxication as they accumulate in the body.

Due to the described factors, gold or platinum alloys are often the only possible solution for patients prone to polyetiological contact intolerance.

The main advantage of noble metals is their almost lifelong service life. Well, the disadvantages include, perhaps, their too high cost, in comparison with analogue offers made from cheaper components.

The main area of ​​application of noble metals is bridges and stamped crowns. Platinum is an ideal solution for the manufacture of cast-type clasp prosthetic fragments, inlays and clasp retainers.

Properties of noble alloys

The ideal option, according to most dentists, is expensive gold-platinum alloys.
They have impeccable mechanical and physical properties, high biocompatibility and are well combined with ceramics. The most famous noble alloys produced in Russia are “Plagodent” and “Plagodent Plus”. Palladium in combination with gold forms alloys with excellent physical and mechanical properties and high corrosion resistance. They have a decent yield strength and high tensile strength, so long bridges and permanent elements of locking joints are made from them. In appearance they resemble base alloys. Only 10% palladium in the composition gives the alloy a white color, similar to steel.

Working with palladium structures requires certain skills from the dentist due to the high melting point of the alloy and special casting techniques. Soldering and laser welding should be avoided. Gold-palladium alloys are cheaper than gold-platinum alloys: due to different densities, the difference in cost can reach 2-2.5 times.

The percentage of noble metal in the alloy affects corrosion resistance and biocompatibility. The cost of a prosthesis can only be reduced by switching to non-precious alloys. A noble alloy may contain a high or low gold content, or may not contain this element at all, as, for example, in silver-palladium compositions.

What determines the color of noble alloys?

Doctors pay attention to color. It is believed that a very yellow alloy containing a lot of gold improves the color of ceramics: the oxides of such alloys are easily coated with a thin layer of opaque and look aesthetically pleasing. A patient who observes the golden color of the crown frame at intermediate stages has no doubt about the need to purchase such an expensive prosthesis.

In some noble alloys, the proportion of palladium, platinum or silver is increased, so they lose their yellow color, but remain just as strong. Such varieties are suitable for the manufacture of extended bridges, with or without implant support. If you are going to install a single crown, you can get by with an option with a high gold content and a low content of platinum group metals.

Alloys with fewer noble components have a pronounced yellow color and do not have such good properties as white alloys. They contain a high content of indium, which in combination with palladium gives a bright straw color. They do not have sufficient elasticity and corrosion resistance. They are used mainly in China and India on a massive scale to reduce the cost of dentures.

Ignoble

Base metals have a single purpose in their use - reducing the cost of prosthetic structures. They are based on environmentally friendly components that can replace gold or platinum.

Stainless steel, chrome-cobalt combinations of metals, and nickel-chromium compounds are best suited for this.

Such components are the most popular metals in orthodontic practice. In addition, they have excellent alloying characteristics, so that the composition can be given any properties.

This is interesting: Installing a ceramic inlay to restore tooth integrity

The main advantage of stainless steel is its low cost. Disadvantages can be considered:

  • heavy specific gravity - density about 8 grams per cubic cm;
  • high chemical activity;
  • the ability to provoke allergic reactions;
  • tendency towards galvanosis.

Application area:

  • fixed type of prosthetics;
  • personal crown frames;
  • cast dental systems;
  • facets;
  • sleeves of a standard type, which are a template blank for the manufacture of stamped crown products;
  • clasps for fixing dentures and bracket systems;
  • filling matrices;
  • separation plates;
  • soldered bridges;
  • orthodontic wire.

Base compounds have good mechanical and chemical properties:

  • low density;
  • fluidity is within normal limits;
  • meltability.

Cobalt chromium alloy in dentistry

(cobalt-chromium alloy, cobalt-chromium alloy)

COMPOUND:

  • cobalt 66-67%, alloy base, hard, durable and light metal.
  • chromium 26-30%, introduced mainly (as in steel) to increase corrosion resistance.
  • nickel 3-5%, increases ductility, malleability, toughness of the alloy, improves the technological properties of the alloy.
  • molybdenum 4-5.5%, increases the strength of the alloy.
  • manganese 0.5%, which increases strength and casting quality, lowers the melting point, and helps remove toxic sulfur compounds from the alloy.
  • carbon 0.2%, reduces the melting point and improves the fluidity of the alloy.
  • silicon 0.5%, improves the quality of castings, increases the fluidity of the alloy.
  • iron 0.5%, increases fluidity, improves casting quality.

PROPERTIES of KHS dental alloy:

It is distinguished by good physical and mechanical properties, low density (and, accordingly, the weight of restorations) and excellent fluidity, allowing the casting of openwork products of high strength.

Melting point is 1458 C

The alloy is resistant to abrasion and retains a mirror-like shine for a long time.

Cobalt-chrome alloy in dentistry

Used for cast crowns, bridges, solid clasp dentures, frames of metal-ceramic dentures, removable dentures with cast bases, splinting devices, cast clasps.

Metal-ceramics metal composition in dentistry

metal alloy

metal ceramics in dentistry.

Metals

Metals are a group of elements that differ from other groups of substances.

They have variables such as:

— high electrical conductivity; - malleability; — high thermal conductivity; — surface gloss with appropriate processing; — complete opacity; - plasticity.

These aspects are characteristic of both ferrous and non-ferrous metals used in dentistry. Black ones have a dark gray color, their hardness, melting point and density are high.

Colored ones are light (red, yellow, white), more plastic than black ones, less hard, melting points are usually lower.

People of color belong to one of the following groups:

- lungs; - heavy.

The first class includes lithium, barium, beryllium, potassium, sodium, magnesium, calcium, and aluminum. They are characterized by low density in the range of 0.53-3.5. The heavy group includes zinc, tin, copper, nickel, and lead. The density of these metals ranges from 7.14 to 11.34. Titanium is included in the light group, its density is higher - 4.5.

Separately from the colored ones, rare earth and noble ones are distinguished.

These metals are divided into three classes according to their crystal lattice structure:

— the most common is cubic body-centered (vanadium, chromium, molybdenum); — face-centered cubic (lead, copper, nickel); — hexagonal close-packed (zinc and titanium).

Alloys

To obtain a combination of necessary characteristics that one metal cannot provide, an alloy is created from several. There are not only metal alloys, but also non-metallic ones. The former necessarily include a metal or several, or a non-metal and a metal, the latter consist of substances such as glass ceramics, glass and porcelain.

Depending on the number of components, alloys are divided into the following groups:

- binary, if the composition includes 2 elements; - triple - if 3.

And so on according to a similar principle.

The interaction of atoms in an alloy can take place according to several scenarios. Some components, when fused, retain the appearance and characteristics of the grain structure - these are mechanical mixtures. If the particles dissolve in each other, then these are solid solutions. The last group includes most dental alloys, including gold.

Another method of classification is separation by melting point:

- low-melting - up to 300 degrees; - refractory noble - up to 1100; - refractory base - more than 1200.

Nickel-chromium alloys in dentistry

Alloys in which the main element is Ni. The elements of this alloy, in addition to nickel, are Cr (at least 20%), Co and molybdenum (Mo) (4%).

The properties of the nickel alloy are close to the cobalt alloy.

Used: for casting fixed dentures and removable denture frames.

Today, the use of nickel alloys is limited due to their high allergenicity.

Titanium alloys in orthopedic dentistry

In dentistry, both pure titanium (99.5%) and its alloys are used.

The use of orthodontic wire in modern medicine

Until the 50s of the last century, orthodontists used only precious metals for their purposes. Other materials did not meet safety parameters for humans or did not withstand the internal oral environment. The emergence of orthodontic wire with a wide range of mechanical properties and at the same time a high degree of resistance to corrosive influences in the oral cavity has made it possible to solve many problems and reduce the cost of manufacturing springs and rings in removable devices, as well as braces and arches.

Basic properties of orthodontic wire

  • Corrosion resistance;
  • Strength and elasticity. Kink resistance;
  • High stability of mechanical properties;
  • Extreme accuracy of parameters.

These properties allow for great variation through cold working and annealing. Stainless steel wire is softened by annealing and hardened by cold working. The resulting material has high elasticity and deformability.


Dental orthodontic stainless steel wire

Dental wire with a diameter of 0.6 or 0.8 mm is used as ligature wire. Wider diameters (1 mm or 1.2 mm) are used for the manufacture of removable dentures and maxillofacial devices.

In the manufacture of orthodontic prostheses or devices, there is often a need to connect individual elements or structures by welding or soldering. It is important to understand that prolonged exposure to high temperatures can change the properties of stainless steel, therefore the technologies that will be used to connect elements must eliminate prolonged exposure to high temperatures on metal parts of the structure. Typically, stainless steel elements are joined using hard solder.

Auxiliary alloys used in orthopedic dentistry

Bronze is an alloy of copper and tin. Aluminum bronze (aluminum instead of tin) is used in dentistry. It is used to make ligatures for splinting jaw fractures.

Brass is an alloy of copper and zinc; pins for collapsible models are made from it.

Magnalium is an alloy of aluminum and magnesium; aircraft parts are made from it (the alloy is very light and durable). In dentistry, articulators and some cuvettes are made from it.

Amalgams are an alloy of metal and mercury. Used for filling.

The topic is too broad; amalgam in dentistry will be discussed in a separate article.

Reviews

According to statistics, most patients prefer orthodontic structures made of metal ceramics.

This is due to acceptable quality, durability and affordable price.

We will be grateful if you share your opinion about any metal used in dentistry. You can leave feedback in the comments to this article.

If you find an error, please select a piece of text and press Ctrl+Enter.

Tags metals fixed dentures

Did you like the article? stay tuned

Low-melting alloys in orthopedic dentistry

Low-melting alloys (Mellota, Wood, Rose) - contain Bismuth, Tin, Lead

– their melting point is about 70 C.

They are used for dies when stamping crowns, counter dies, and making collapsible models.

Low-melting metals in dentistry

Wood's alloy.

Melting point 68 C.

Composition: Bismuth – 50%, Lead – 25%, Tin – 12.5%, Cadmium – 12.5%.

Toxic because it contains cadmium.

Mellot alloy.

Melting point 63 C

Composition: Bismuth – 50%, Lead – 20%, Tin – 30%.

Rose alloy for dentistry.

Melting point 94 C.

Composition: Bismuth – 50%, Lead and Tin 25% each.

Definition of structure

Using microscopic and macroscopic analyses, you can find out the structure of metals. Macroanalysis helps determine:

  • micro- and macroscopic metal defects;
  • chemical composition (heterogeneity of various alloy elements);
  • structure (heterogeneity of alloys resulting from heat treatment).

Thanks to the microscopic method of examination, it is possible to establish:

  • the shape and dimensions of any structural elements of the alloy;
  • microcracks that violate the integrity of the material;
  • structures typical for certain processing methods;
  • additives of non-metallic origin;
  • a change in structure that occurs under thermal influence.

Steel for dental instruments

Tool steel – contains carbon from 0.7% or more.

It is characterized by high strength and hardness (after special temperature treatment).

The addition of tungsten, molybdenum, vanadium and chromium to steel makes the steel capable of cutting well at high speeds. This steel is used for burs and cutters.

Tungsten carbide is not an alloy. A chemical compound of tungsten with carbon (chemical formula WC). Comparable in hardness to diamond. Used for the production of armor-piercing tank shells. And also for carbide dental burs.

Zirconium metal in dentistry

Zirconium dioxide is also not an alloy. Chemical compound of zirconium metal with oxygen. Its chemical nature is similar to ceramics, but it is harder and more durable. In dentistry they are used for the manufacture of milled dentures.

Rating
( 2 ratings, average 5 out of 5 )
Did you like the article? Share with friends:
For any suggestions regarding the site: [email protected]
Для любых предложений по сайту: [email protected]